Journal of Pure and Applied MicrobiologyVol. 9 No. Special Edition May. 2015

Structure Characteristics of Acidic Pretreated Fiber and Self-bind Bio-boards for Public Health

Zhi Lin1, Sheng-Bo Ge1, Dong-Li Li1 and Wan-Xi Peng1,2*

1School of Materials Science and Engineering, Central South University of Forestry and Technology, Changsha 410004, China. 2State Key Laboratory of Pulp and Paper Engineering, South China University of Technology, Guangzhou 510640, China.

Received on 20 Feburary 2015 and accepted on 15 April 2015



Abortion, which has been induced by indoor formaldehyde pollution, is more and more severely threating public health. To fundamentally eliminate indoor formaldehyde pollution, wood fiber was done by acid pretreatment and self-bind precess, and analyzed by FT-IR and SEM. The results shown that the bond strength firstly increased and then decreased with the increase of pretreatment time, reached the maximum value 0.52 MPa (HOOC-COOH) for 10h and 0.82 MPa (1%CH3COOH) for 15h. lignin did not change during the acid pretreatment, ˛- glycosidic bond of cellulose decreased, other groups all increased during acid pretreat. And the active groups, lignin and cellulose all took part in the chain reaction during self-bind precess. Wood fiber was better done by 1% CH3COOH pretreatment than by 1% CH3COOH pretreatment in favor of self-bind bio-boards.

Keywords : FT-IR, SEM, Self-bind bio-boards, Formaldehyde pollution, Abortion.